NB/T 47052-2016: Simple pressure vessels
NB/T 47052-2016
NB
ENERGY INDUSTRY STANDARD OF
THE PEOPLE’S REPUBLIC OF CHINA
ICS 23.020.30
J 74
Simple pressure vessels
简单压力容器
ISSUED ON: AUGUST 16, 2016
IMPLEMENTED ON: DECEMBER 01, 2016
Issued by: National Energy Administration
Table of Contents
Foreword ... 5
1 Scope ... 6
2 Normative references ... 7
3 Terms and symbols ... 8
4 Product type and product type code ... 11
5 General provisions ... 12
6 Materials ... 16
7 Design ... 18
8 Manufacturing, inspection, acceptance ... 21
Appendix A (Normative) Declarations of conformity and amendments to standards 34
Appendix B (Informative) Product type code ... 35
Appendix C (Informative) Commonly used welded joint structures ... 37
Simple pressure vessels
1 Scope
1.1 This standard specifies the construction requirements for the type and materials,
design, manufacturing, inspection and acceptance of simple pressure vessels
(hereinafter referred to as "vessels").
1.2 This standard applies to mass-produced vessels, that meet the following conditions:
a) The design pressure is less than or equal to 1.6 MPa;
b) The design temperature is greater than or equal to -20 °C; the maximum operating
temperature is less than or equal to 150 °C;
c) The volume is less than or equal to 1.0 m3;
d) The product of working pressure and volume is less than or equal to 1.0 MPa·m3;
e) The medium is air, nitrogen, carbon dioxide, inert gas, water vapor evaporated
from medical distilled water, or a mixture of the above gases (vapors); the
medium is allowed to contain other components such as oil that are not enough
to change the characteristics of the medium, but its flash point or ignition point
shall be 30 °C higher than the maximum working temperature of the vessel,
without affecting the compatibility with the material;
f) The structure meets the requirements of 4.1.1.
1.3 The following products do not fall within the scope of this standard:
a) Vessels used in military equipment, nuclear facilities, aerospace vehicles, offshore
facilities, ships;
b) Non-independent pressure-bearing parts on the machine (such as compressor
cylinder, etc.);
c) Fire extinguisher;
d) Quick opening vessel;
e) Mobile vessels;
f) Vessels that require fatigue analysis and design;
c) The design organization shall keep the following design documents of the vessel
for reference, meanwhile the retention period shall not be less than the design
service life of the vessel:
1) Design drawing;
2) Design calculations, including at least volume calculations, strength
calculations or explosion test reports (including quality certification
documents for test sample materials, manufacturing process documents,
inspection records, test records, etc.), design service life, safe discharge
volume calculation, calculation of safety valve displacement, etc.;
3) Design instructions, including at least the basis for selecting design parameters,
selection of materials, selection of accessories, manufacturing technical
conditions, inspection requirements, etc.;
4) Installation, use, maintenance instructions, including at least the maximum
working pressure, maximum working temperature, designated use, installation
requirements, design service life, safety maintenance points, etc.
5.2.2.3 Responsibilities of the manufacturer:
a) The manufacturer shall manufacture according to the design drawings; if the
original design needs to be modified, a written document agreeing to the
modification shall be obtained from the original design organization, meanwhile
the modified parts shall be recorded in detail.
b) The manufacturer shall formulate a complete quality plan before batch
manufacturing of vessels, which at least includes manufacturing process control
points, inspection items, qualification indicators.
c) During the manufacturing process, the manufacturer shall ensure the stability of
the manufacturing process; conduct specific inspections and tests on the vessel in
accordance with this standard and drawings; issue an inspection report; be
responsible for the accuracy and completeness of the report; issue a product
certificate after passing the inspection.
d) The manufacturer shall keep the type test report and certificate of the vessel for
long-term reference; each batch of vessels it produces shall have at least the
following relevant technical documents for reference. The retention period of the
technical documents shall not be less than the design service life of the vessel,
and no less than five years:
1) Material quality certificate for pressure components;
2) General manufacturing process documents;
3) Welding process documents;
4) Inspection and test records during the manufacturing process and after
completion of the vessel;
5) Original design drawings and as-built drawings of the vessel.
5.2.2.4 Responsibilities of inspection agencies
The institutions and their supervisory inspectors that conduct supervisory inspections
of vessels, within the jurisdiction of TSG 21, shall perform corresponding work
responsibilities, in accordance with the provisions of the specifications during
supervisory inspections; they shall be responsible for the completeness and accuracy of
the inspection reports issued.
5.3 General provisions for design
5.3.1 Design methods are divided into calculation methods and test methods. The wall
thickness of the pressure components of the vessel is calculated according to the rules
of the corresponding chapter of GB 150.3. The wall thickness of the main pressure
components, such as the cylinder, convex head, flat cover, etc. of the vessel, is
determined by the bursting test using the physical vessel sample, as the test method.
Austenitic stainless steel vessels are not allowed to be designed using test methods.
5.3.2 The overall design drawing of the vessel shall indicate at least the following:
a) Name of the specification and standard based on;
b) Vessel name;
c) Design methods;
d) Material designation and material requirements of pressure components;
e) Design conditions, including design temperature, design pressure, working
pressure, design service life, medium, corrosion allowance, etc.;
f) Main characteristic parameters, including volume, weight, etc.;
g) Welding methods and requirements; the degree of mechanization of the welding
method of longitudinal butt joints of pressure components and the degree of
mechanization of the welding method of non-full-section penetration pipe seats
when designing the calculation method;
h) Anti-corrosion requirements (if necessary);
i) Pressure test requirements, including test pressure, medium, etc.;
6.3 The negative deviation of steel plate and steel pipe materials shall comply with the
provisions of the corresponding material standards.
6.4 The materials, usage conditions, allowable stress of non-welded parts such as studs
and nuts shall be in accordance with the provisions of the corresponding chapters of
GB 150.
6.5 The material of the permanent backing plate shall be the same or similar to the steel
designation of the weldment.
6.6 The welding materials used shall ensure that the performance of the welded joint
meets the design requirements.
7 Design
7.1 Design of wall thickness
7.1.1 Design of calculation method
7.1.1.1 The design pressure of the vessel shall not be lower than its working pressure.
7.1.1.2 For vessels equipped with safety valves, the design pressure shall be determined
according to the following steps:
a) Determine the safety valve's setting pressure pz, according to the working pressure
pw of the vessel, take pz = (1.05 ~ 1.1) pw;
b) Take the design pressure p of the vessel to be equal to or slightly greater than the
setting pressure pz.
7.1.1.3 The calculated thickness δ of the pressure component shall be calculated,
according to the relevant formulas of GB 150.3; the allowable stress shall be as
specified in Table 1.
7.1.1.4 If the longitudinal butt welded joint of a pressure component is manually welded,
the calculated thickness of the component shall be increased by 15%.
7.1.1.5 Take the design thickness of the pressure component of the vessel, which is
designed using the calculation method δd = δ + C2.
7.1.1.6 Flanges, flange covers and other pressure components can be designed or
selected, with reference to other relevant standards.
7.1.2 Design of test method
7.1.2.1 The design organization shall conduct bursting tests on the physical samples of
vessels, which are trial-produced by the client; it shall proceed according to the steps
7.1.2.4 Determine the design thickness δd, based on the actual measured wall thickness
of each main pressure component, as measured on the sample that passed the bursting
test.
7.1.2.5 The design organization shall fully consider the repeatability of bursting test
results, as well as the differences in mechanical properties between different batches of
materials of the same steel designation.
7.1.3 Marking of thickness
7.1.3.1 Calculation method for designed vessels:
a) The minimum forming thickness of the convex head shall be marked on the design
drawing. Whether the nominal thickness of the convex head is marked on the
design drawing is decided by the design organization;
b) The nominal thickness and minimum formed thickness of other pressure
components shall generally be marked on the design drawing; for some small
vessels, as long as the minimum formed thickness meets 5.3.4, the strength
requirements can be guaranteed. For the main pressure components such as
cylinders, flat covers, it may only mark the minimum forming thickness.
7.1.3.2 Vessels designed by test method
The minimum forming thickness of the main pressure components of the vessel
designed by the test method shall be marked on the design drawing; whether the
nominal thickness of the main pressure component is marked on the design drawing is
decided by the design organization.
7.2 Opening and opening reinforcement
7.2.1 In addition to the necessary process nozzle openings, the vessel can be equipped
with inspection holes such as observation holes and hand holes, as needed. A drain
outlet shall be provided at the lowest point at the bottom of the vessel.
7.2.2 The maximum allowable diameter of the opening on the vessel shell is dop ≤ Di/2.
Except for 7.2.3, all other provisions for openings and reinforcements shall comply with
the corresponding chapters of GB 150.3.
7.2.3 All openings shall avoid butt welding joints. The distance -- between the edge of
the weld at the opening and the edge of other welds -- shall not be less than 4 times the
actual measured wall thickness of the opening and not less than 20 mm.
7.3 Welded structure
7.3.1 All main body welding joints must adopt full penetration type.
7.3.2 See Appendix C for commonly used welded joint structures.
b) The reinforcement ring complies with the requirements of JB/T 4736;
c) The pipe flange complies with the requirements of HG/T 20592 ~ 20635.
8.1.2 Type test
Vessels shall be type tested by a type testing agency, which has corresponding
qualifications; type testing shall be in accordance with the provisions of 8.4.
8.1.3 Material substitution
The manufacturer shall obtain written approval, in advance from the original design
organization when substituting materials for pressure components. Substitution of
materials must be recorded in detail on the as-built drawings.
8.2 Manufacturing
8.2.1 Material re-inspection and sign transplantation
8.2.1.1 Reinspection of materials
8.2.1.1.1 The following materials shall be re-inspected:
a) The authenticity of the quality certificate cannot be determined or the performance
and chemical composition of the main pressure component materials are doubtful;
b) S30408 open plate for manufacturing main pressure components
c) When the design requires.
8.2.1.1.2 The mechanical properties of the S30408 open flat plates shall be retested
according to the batch number (for use of whole coil, it shall cut a set of retesting
specimens from the corresponding open flat plates at the head, middle, tail of the coil
for after the flat opening operation; for use of non-whole coil, it shall cut a set of
retesting specimens from the end of the open flat plate). For situations where retesting
is required in items a) and c) in 8.2.1.1.1, the chemical ingredients shall be retested
according to the heat number; the mechanical properties are rechecked by batch.
8.2.1.1.3 The results of material retesting shall comply with the provisions of the
corresponding material standards or the requirements of the design documents.
8.2.1.2 Material sign transplantation
Materials used to manufacture pressure components shall be marked traceable by batch.
8.2.2 Group batching
Vessels of the same model, drawing number, welding joint using the same welding
process can be produced in batches. The requirements for group batching are as follows:
a) Group batching time: Continuous production time shall not exceed 15 days:
b) Batch quantity: For vessels with an inner diameter of the shell Di ≤ 400 mm, a
batch shall not exceed 1000 units according to the production sequence; for
vessels with an inner diameter Di > 400 mm, a batch shall not exceed 500 units
according to the production sequence.
8.2.3 Forming and assembly
8.2.3.1 Forming
8.2.3.1.1 The manufacturer shall determine the processing allowance based on process
conditions and the actual thickness of the steel, to ensure that the measured minimum
forming thickness of the pressure components of the vessel is not less than the design
thickness.
8.2.3.1.2 When the selected nominal thickness cannot guarantee the minimum forming
thickness, the manufacturer shall consider selecting an appropriate steel thickness.
8.2.3.2 Groove
The groove shall meet the following requirements:
a) The groove surface must not have defects such as cracks, delamination, inclusions,
etc.;
b) Before welding, oxide scale, oil stain, melting sl...